However, the value of magnetoresistance increased apparently after annealing and was 1.74 times the unannealed sample.
而退火後磁電阻值則明顯增加，是未退火時的1.;74倍；
From the PL measurement the near band edge(NBE) emission and deep-level(DL) emission are observed in unannealed AZO thin films.
未退火樣品的光致發(fā)光(PL)譜由361 nm附近的紫外帶邊發(fā)射峰和500 nm附近的深能級發(fā)射峰組成。
The experimental results indicated that the film resistivity of the sample annealed was reduced significantly and only one 3.17 of the unannealed.
實騐結(jié)果表明：退火後樣品的薄膜電阻率顯著減小，是未退火樣品薄膜電阻率的3.;17分之一；
XRD structural analysis shows thatpeak intensity of the annealed sample is greater than that of the unannealed one which demonstrated an increase of crystallinity.
XRD結(jié)搆分析顯示，退火後薄膜樣品的峰值強度大於未退火樣品的強度，說明樣品結(jié)晶度增強。