solidification cracking

基本解釋

Solidification cracking is a critical problem during the welding of nickel-based corrosion-resistance materials.
鎳基耐蝕材料的焊接結晶裂紋是該類材料焊接性研究中的關鍵性問題。
Heater leak occurs by direct reason of the stress corrosion cracking, while by other reasons of solidification cracking, small fusion depth of welding joint and non…
應力腐蝕裂紋是造成加熱器泄漏的直接原因，結晶裂紋、焊縫熔深小及坡口底部未熔透也是加熱器泄漏的原因。
The solidification analysis on shot cracking proved that hot cracking was influenced by the cooling rate of alloy under uncompensated stage of solidification process.
理論分析認為，合金在不可補縮區(qū)的冷卻速率變化是改變合金熱裂程度的重要因素。